Effects of strain rate on the microstructure evolution and mechanical response of magnesium alloy AZ31

详细信息    查看全文

• 作者：Ling Li^a ; Ondrej Murá ; nsky^b ; ^c ; E.A. Flores-Johnson^d ; Saurabh Kabra^e ; Luming Shen^a ; Gwé ; naë ; lle Proust^a ; ^{gwenaelle.proust@sydney.edu.au}
• 关键词：Magnesium alloy ; Split Hopkinson pressure bar ; Microstructure ; EBSD ; Neutron diffraction ; Crystal plasticity
• 刊名：Materials Science and Engineering: A
• 出版年：2017
• 出版时间：27 January 2017
• 年：2017
• 卷：684
• 期：Complete
• 页码：37-46
• 全文大小：1689 K
• 卷排序：684

文摘

The effects of strain rate on the mechanical behaviour and microstructure evolution of extruded Mg AZ31 alloy are investigated here for strain rates ranging from 0.0001 s−1 to 4000 s−1. High strain rate compression testing was performed using a split Hopkinson pressure bar apparatus. The microstructure and texture evolution were characterised by using electron backscatter diffraction (EBSD) and neutron diffraction. The results show that the yield strength increases by roughly 55% from the quasi-static to the high strain rate regime while the plateau stress increases by roughly 35%. After compression along the extrusion direction, the deformed textures of both quasi-static and high strain rate loading samples are similar, showing that a large portion of grains have been reoriented through the activation of tensile twinning. However, a detail EBSD analysis suggests that there is a higher fraction of secondary compressive twins in high strain rate deformed specimens at 16% strain. A visco-plastic self-consistent (VPSC) model, which incorporates the composite grain scheme to account for twinning, is employed to model the mechanical response and texture evolution, and to elucidate the collaborative nature of the slip-twinning deformation. Using only a single set of parameters, the VPSC model successfully reproduces the stress-strain curves at all tested strain rates, and more importantly, captures the texture and twin volume fraction evolutions. The simulation results suggest that under quasi-static and high strain rate loadings, the dominant slip systems are different in both untwinned grains and tensile twins. The results also suggest that twins are formed at a lower strain at high strain rates when compared to quasi-static loading.