The effect of minor additions of Si to a Ti–Cu–Ni–Zr metallic glass was studied.
An optimum glass-forming ability occurs for 0.5 at% Si.
None of the GFA criteria predicts this optimum.
It's explained considering the increased thermal stability and formation of Ti5Si3.
The alloy with 2 at% Si formed composites with enhanced mechanical properties.