Tensile bond strengths of composites to a gold-palladium alloy after thermal cycling

详细信息    查看全文

• 作者：Jeffrey Chai Chang ; Sheila H. Koh ; John M. Powers ; Joseph H. Duong
• 关键词：AA ; Arachidonic acid ; ACE ; Antigen capture enzyme immunoassay ; ADP ; Adenosine diphosphate ; AGT ; Acquired Glanzmann's thrombasthenia ; DAT ; Direct anti-globulin test ; MoAb ; Monoclonal antibodies ; PTLPD ; Posttransplantation lymphoproliferative disorder
• 刊名：The Journal of Prosthetic Dentistry
• 出版年：2002
• 出版时间：March 2002
• 年：2002
• 卷：87
• 期：3
• 页码：271-276
• 全文大小：157 K

文摘

Statement of Problem. Many different materials and methods have been used to fabricate or repair veneer facings with composites, but only a few of these have been studied. Purpose. This study compared the tensile bond strengths of composites to a gold-palladium alloy with the use of several surface treatment methods. Material and Methods. Forty alloy specimens were cast in Eclipse (52 % gold and 37.5 % palladium) in the form of truncated cones. These specimens were divided equally into 4 groups. In group I, the bonding surfaces of the metal cones were treated with Silicoater MD. Truncated cones of Dentacolor composite were bonded to the metal surfaces and light-polymerized. In group II, the bonding surfaces of the metal cones were air-particle abraded with 50 μm aluminum oxide and coated with C&B Metabond. Truncated cones of Epic-TMPT composite were bonded to the metal surfaces and light-polymerized. In group III, the bonding surfaces of the metal cones were air-particle abraded with CoJet-Sand. Truncated cones of Pertac-Hybrid composite were bonded to the metal surfaces and light-polymerized. In group IV, the bonding surfaces of the metal cones were air-particle abraded with CoJet-Sand. Truncated cones of Visio-Gem were bonded to the metal surfaces and light-polymerized. After 24 hours of water immersion at 37°C and 1000 thermal cycles in water at 5°C and 55°C, tensile forces were applied to all specimens with a universal testing machine. Analysis of variance was applied to the data (P<.05), and differences among means were determined with a Tukey-Kramer interval of 5.4 MPa. Results. Tensile bond strengths in MPa were as follows: Dentacolor, 14 ± 5; Epic-TMPT, 12 ± 4; Pertac-Hybrid, 13 ± 5; and Visio-Gem, 18 ± 4. The tensile bond strength of Visio-Gem was significantly higher than that of Epic-TMPT, but no differences were found among Dentacolor, Pertac-Hybrid, and Epic-TMPT (P<.05). Conclusion. Within the limitations of this study, all 4 bonding systems tested produced high bond strengths between composites and a gold-palladium alloy after thermal cycling. (J Prosthet Dent 2002;87:271-6.)