Synthesized austenitic stainless steel starting from blended elemental powders.
As-milled powders with low Ni content show formation of only the stress-induced martensite phase.
Fully homogeneous austenite phase was synthesized at 20% Ni content.
The amount of austenite phase increased after annealing.