Improving the compatibility of an Y-TZP/porcelain system using a new composite interlayer composition

详细信息    查看全文

• 作者：Sheila P. Passos^a ; ^{passos@ualberta.ca} ; Bernie Linke^a ; Paul W. Major^a ; John A. Nychka^a ; ^b
• 关键词：Flexural strength ; Cooling rate ; All-ceramics ; Y-TZP ; Delamination
• 刊名：Journal of the Mechanical Behavior of Biomedical Materials
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：65
• 期：Complete
• 页码：11-19
• 全文大小：1783 K
• 卷排序：65

文摘

The aim of this study was to evaluate the effects of different cooling procedures and a new composite interlayer composition on the flexural strength, and veneer delamination resistance, of an all-ceramic veneered translucent Y-TZP core. One hundred twenty bar-shaped specimens of a translucent Y-TZP ceramic were prepared and divided into three groups: (1) no composite interlayer; (2) a glass interlayer (silica-based glass); (3) a mixed composite interlayer of glass and porcelain veneer material. A veneering porcelain (with and without a composite interlayer) was applied on the specimen surface and sintered. Each core–veneer group was cooled using a rapid or a slow cooling rate. All specimens were tested in four-point bending. Data were statistically analyzed using two-way ANOVA, followed by Post-Hoc tests with Bonferroni correction (α=0.05) and Weibull analysis. The group with no interlayer using the rapid cooling technique exhibited the highest flexural strength. However, with low reliability and the greatest delaminated area of porcelain under tension. A glass interlayer between porcelain veneer and zirconia core presents as a good alternative for maintaining flexural strength and porcelain veneer delamination resistance in zirconia based restorations.