Compliant alkali silicate sealing glass for solid oxide fuel cell applications: Thermal cycle stability and chemical compatibility
详细信息 查看全文
- 作者：Yeong-Shyung Chou ; E.C. Thomsen ; R.T. Williams ; J.-P. Choi ; N.L. Canfield ; J.F. Bonnett ; J.W. Stevenson ; A. Shyam ; E. Lara-Curzio
- 关键词：Sealing glass ; Leak rate ; Coating ; SOFC
- 刊名：Journal of Power Sources
- 出版年：2011
- 出版时间：1 March 2011
- 年：2011
- 卷：196
- 期：5
- 页码：2709-2716
- 全文大小：905 K
文摘
An alkali silicate glass (SCN-1) is currently being evaluated as a candidate sealing glass for solid oxide fuel cell (SOFC) applications. The glass containing 17 mole % alkalis (K2O and Na2O) remains vitreous and compliant during SOFC operation, unlike conventional SOFC sealing glasses, which experience substantial devitrification after the sealing process. The non-crystallizing compliant sealing glass has lower glass transition and softening temperatures since the microstructure remains glassy without significant crystallite formation, and hence can relieve or reduce residual stresses and also has the potential for crack healing. Sealing approaches based on compliant glass will also need to satisfy all the mechanical, thermal, chemical, physical, and electrical requirements for SOFC applications, not only in bulk properties but also at sealing interfaces. In this first of a series of papers we will report the thermal cycle stability of the glass when sealed between two SOFC components, i.e., a NiO/YSZ anode supported YSZ bilayer and a coated ferritic stainless steel interconnect material. High temperature leak rates were monitored versus thermal cycles between 700 and 850 °C using back pressures ranging from 1.4 to 6.8 kPa (0.2–1.0 psi). Isothermal stability was also evaluated in a dual environment consisting of flowing dilute H2 fuel versus ambient air. In addition, chemical compatibility at the alumina and YSZ interfaces was examined with scanning electron microscopy and energy dispersive spectroscopy. The results shed new light on the topic of SOFC glass seal development.