文摘
Fe-18Cr-8Ni and Fe-18Cr-8Ni-1Y (at%) stainless steel powders were nanostructured by mechanical alloying from elemental powders and subjected to 90xA0;min annealing treatments at various temperatures. The microstructural evolutions as a function of alloy compositions and temperatures were investigated by in-situ and ex-situ x-ray diffraction experiments, transmission electron microscopy and focused ion beam microscopy. The dependence of hardness on the microstructure was utilized to study the mechanical changes. It was found that the resulting microstructures by mechanical alloying were bcc solid solution, the so-called α’-martensite structure. The high temperature in-situ x-ray diffraction experiments showed that the martensite-to-austenite reverse phase transformation was completed above 800 and 900xA0;°C for Fe-18Cr-8Ni and Fe-18Cr-8Ni-1Y steels, respectively. A partial or complete retransformation to martensite was observed upon cooling to room temperature. Annealing of nanocrystalline Fe-18Cr-8Ni steel yielded grain growth reaching to micron sizes at 1100xA0;°C while addition of 1xA0;at% yttrium stabilized the microstructure around 160xA0;nm grain size and 6xA0;GPa hardness after 90xA0;min annealing at 1200xA0;°C.