Effect of Ba-dopant on dielectric and energy storage properties of PLZST antiferroelectric ceramics

详细信息    查看全文

• 作者：Ran Xu ; ^{jzgxuran@126.com} ; Qingshan Zhu ; Jingjing Tian ; Yujun Feng ; Zhuo Xu ; ^{xuzhuo@xjtu.edu.cn}
• 关键词：Antiferroelectric ceramics ; Energy storage ; Dielectric tunability
• 刊名：Ceramics International
• 出版年：2017
• 出版时间：1 February 2017
• 年：2017
• 卷：43
• 期：2
• 页码：2481-2485
• 全文大小：2050 K
• 卷排序：43

文摘

(Pb0.94-xBaxLa0.04)[(Zr0.7Sn0.3)0.88Ti0.12](x=0, 0.02, 0.04, 0.06) were fabricated and the effect of Ba content on the dielectric and energy storage properties was studied. The Ba dopant will weaken the stability of AFE phase and thus lower the transition field. As a result, the recoverable energy density declines while the hysteresis loop will be slimmer. Also, the Curie temperature will decrease with increasing Ba content but the maximum dielectric constant increases. The temperature dependence of the energy storage properties and dielectric tunability when x=0.06 were studied. The stored and recoverable energy density both decline but the efficiency increases with temperature rise. The dielectric tunability is promising when x=0.06 at 20 °C but soon becomes weaker at 80 °C.