文摘
Lithium disilicate and Zirconia ceramics offer a high level of accuracy when used in prosthetic dentistry. Their bonding using different resins is highly dependent on micro-mechanical interlocking and adhesive chemical bonding. Investigation of the performances of high strength ceramics when their surface is modified for chemical and mechanical bonding is then required. The aim of this study is to investigate the possibility of using laser for surface treatment of different high strength CAD/CAM ceramics and thus to improve their mechanical and chemical properties. Thirty two CAD/CAM ceramic discs were divided into two different groups: lithium disilicate ceramics (IPS e.max CAD庐, Ivoclar, Vivadent, Italy) and Zirconia ceramics (IPS e.max ZirCAD庐, Ivoclar, Vivadent, Italy). The Laser surface treatment was performed by Carbon Dioxide laser (Dream Pulse Laser庐, Daeshin Enterprise Corp., Korea) at 20 W, 25 W and 30 W CW and by Neodymium Yttrium Aluminum Perovskite laser (Nd:YAP Lokki庐, Lobel Medical, France) at 10 W and 30 Hz. Physical modifications of the irradiated ceramic discs were observed by scanning electron microscopy (SEM) and chemically analyzed by Energy-Dispersive Spectroscopy (EDS). Surface wettability was tested using the water drop test and the crystalline structure was investigated using X-ray diffraction (XRD). The macroscopic observation showed a shinier structure in all the groups, while at the SEM observation only CO2 25 W and 30 W treated groups showed cracks and fissures. In the conditions of this study, CO2 laser and Nd:YAP laser with the parameters used create chemical and physical surface modifications of the ceramics, indicating the possibility of an improvement in adhesion of the tested ceramics.