Study by electron microscopy of proton exchange membrane fuel cell membrane-electrode assembly degradation mechanisms: Influence of local conditions

详细信息    查看全文

• 作者：Laure Gué ; taz ; ^{laure.guetaz@cea.fr} ; Sylvie Escribano ^{sylvie.escribano@cea.fr} ; Olivier Sicardy ^{olivier.sicardy@cea.fr}
• 关键词：Active layer degradation ; Ostwald ripening ; Reverse-current mechanism ; Carbon corrosion ; Platinum dissolution ; Electron microscopy
• 刊名：Journal of Power Sources
• 出版年：2012
• 出版时间：15 August, 2012
• 年：2012
• 卷：212
• 期：Complete
• 页码：169-178
• 全文大小：2332 K

文摘

Observations of microstructural evolution by scanning and transmission electron microscopy in different regions of aged membrane/electrode assemblies (MEA) have shown that degradation is not always uniform through the MEA surface; after load cycling operation, the degradation is more severe in the region located near the air inlet compared to air outlet. After constant load operation the degradation appears more uniform. Two types of microstructural evolution have been observed. The first one consists in the modification of the cathode leading to nanoparticles larger than initially but still well dispersed. The second type of evolution ends up with big agglomerates formed by large Pt particles in the cathode, with also a noticeable degradation of the carbon support, both phenomena being always coupled with the precipitation of Pt particles inside the membrane. The first type of evolution results from the electrochemical Ostwald ripening mechanism and appears when the cathode potential remains low. In contrast, the second one appears when the cathode is locally exposed to a high interfacial potential resulting from the reverse-current mechanism. Hydrogen starvation induced by the load cycles and oxygen crossover that increases with membrane damage, are the two main factors responsible for this severe degradation mechanism.