Determination of Interfacial Heat Transfer Behavior at the Metal/Shot Sleeve of High Pressure Die Casting Process of AZ91D Alloy

详细信息    查看全文

• 作者：Wenbo Yu¹ ; ² ; Yongyou Cao¹ ; ² ; Xiaobo Li¹ ; ² ; Zhipeng Guo¹ ; ² ; Shoumei Xiong¹ ; ² ; ^{smxiong@tsinghua.edu.cn}
• 关键词：High pressure die casting (HPDC) ; Interfacial heat transfer behavior ; Inverse method ; Slow casting speed
• 刊名：Journal of Materials Science & Technology
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：33
• 期：1
• 页码：52-58
• 全文大小：3523 K
• 卷排序：33

文摘

The interfacial heat transfer behavior at the metal/shot sleeve interface in the high pressure die casting (HPDC) process of AZ91D alloy is carefully investigated. Based on the temperature measurements along the shot sleeve, inverse method has been developed to determine the interfacial heat transfer coefficient in the shot sleeve. Under static condition, Interfacial heat transfer coefficient (IHTC) peak values are 11.9, 7.3, 8.33 kW m−2 K−1 at pouring zone (S2), middle zone (S5), and end zone (S10), respectively. During the casting process, the IHTC curve displays a second peak of 6.1 kW m−2 K−1 at middle zone during the casting process at a slow speed of 0.3 m s−1. Subsequently, when the high speed started, the IHTC curve reached a second peak of 12.9 kW m−2 K−1 at end zone. Furthermore, under different slow casting speeds, both the calculated initial temperature (TIDS) and the maximum temperature (Tsimax) of shot sleeve surface first decrease from 0.1 m s−1 to 0.3 m s−1, but increase again from 0.3 m s−1 to 0.6 m s−1. This result agrees with the experimental results obtained in a series of “plate-shape” casting experiments under different slow speeds, which reveals that the amount of ESCs decreases to the minimum values at 0.3 m s−1 and increase again with the increasing casting slow speed.