文摘
An Al-8B-2C master alloy was added into Al-Ti melts to study the reaction of Al3BC phase with Ti. As a result, a new Al-5Ti-0.8B-0.2C master alloy was fabricated. The microstructures were studied by field emission scanning electron microscope (FESEM), X-ray diffraction (XRD) and transmission electron microscope (TEM). The analysis indicates that C-doped TiB2 and B-doped TiC which show macroporous and lamellar morphologies are transformed from Al3BC. The transformation mechanism is also discussed in this work. Furthermore, the grain refinement performance of the Al-5Ti-0.8B-0.2C on A356 alloy was investigated.