Dose dependent modifications in structural and magnetic properties of γ-irradiated nanocrystalline Mn_0.5Zn_0.5Fe₂O₄ ceramics

详细信息    查看全文

• 作者：V. Jagadeesha Angadi^a ; A.V. Anupama^b ; R. Kumar^b ; H.M. Somashekarappa^c ; S. Matteppanavar^a ; B. Rudraswamy^a ; B. Sahoo^b ; ^{bsahoo@mrc.iisc.ernet.in" class="auth_mail" title="E-mail the corresponding author}
• 关键词：Mn-Zn ferrite ; Nanocrystalline Ceramics ; γ-irradiation ; Phase transformations ; Mö ; ssbauer spectroscopy
• 刊名：Ceramics International
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：43
• 期：1
• 页码：523-526
• 全文大小：655 K

文摘

Different doses of γ-radiation can be used to modify the structural and magnetic properties of a host of materials. The Mn_0.5Zn_0.5Fe₂O₄ ceramics samples prepared by the solution combustion route were exposed to different doses of γ-radiation in order to study stability and phase transformations. The creation of defects and building up of strain was observed after medium doses of γ-irradiation (up to 25 kGy) into the single phase pristine samples. However, after 50 kGy of γ-irradiation the locally generated heat drives atomic diffusion, as indicated by the morphological changes in the sample. Furthermore, the sample decomposed into two new stable crystalline phases, α-Fe₂O₃ and ZnFe₂O₄, along with amorphous MnO phase. Besides the structural transformations we have observed the deterioration of magnetic properties at higher doses. Our results are important for understanding the stability and performance of the ferrite based devices used near intense high energy radiation sources.