Controlling the wettability and adhesion of carbon fibers with polymer interfaces via grafted nanofibers

详细信息    查看全文

• 作者：Seokjin Hong^a ; Majid Minary-Jolandan^c ; Mohammad Naraghi^a ; ^b ; ^{naraghi@aero.tamu.edu" class="auth_mail" title="E-mail the corresponding author}
• 关键词：Hybrid composites ; Polymer-matrix composites (PMCs) ; Interface ; Electro-spinning ; Fiber/matrix bond
• 刊名：Composites Science and Technology
• 出版年：2015
• 出版时间：29 September 2015
• 年：2015
• 卷：117
• 期：Complete
• 页码：130-138
• 全文大小：1836 K

文摘

Interfacial properties in carbon fiber composites is one of the key parameters controlling their structural functionality. Here, we introduce a novel method to engineer carbon fiber-epoxy interfaces, via inclusion of nanofibers, towards higher interfacial strength and energy dissipation. In our method, thermally stabilized polyacrylonitrile (PAN) nanofibers are grafted onto carbon fibers via electro-spinning process, followed by nanofiber consolidation via solvent vapor and thermal treatment. These treatments partially dissolves nanofibers along the nanofiber-fiber interface and trigger entropic elasticity in nanofibers, thus, increasing the nanofiber-fiber interactions. The hybridization of carbon fibers with PAN nanofibers increased the interfacial shear strength (IFSS) by ∼48%, from 10.8 ± 2.6 to 15.9 ± 4.9 MPa. Postmortem fractography points to mechanical interlocking between nanofibers and epoxy and reinforcing effects of nanofibers in matrix as root causes of IFSS enhancement. As a result of adding nanofibers to carbon fiber, junction failure mode changes from a dominantly adhesive failure (at epoxy-fiber interface) to dominantly cohesive failure, and failure plane slightly shifts away from epoxy-fiber interface to within the epoxy. Compared to other types of whiskers grown on carbon fibers, such as CNTs, the method proposed here requires low temperatures (below 300 °C), during which no surface damages are expected to accumulate on carbon fibers.