Perovskite Ba0.5Sr0.5Co0.8Fe0.2O3?¦Á (BSCF) hollow fibre membranes were fabricated by a combined phase inversion and sintering technique. The membranes were characterised by XRD, SEM and tested for air separation. The membrane possesses a novel morphology consisting of one dense layer and one porous layer. Oxygen permeation fluxes through the obtained hollow fibre membranes were measured in the temperature range 650-950 ¡ãC using helium sweep gas rates from 50 to 200 mL min?1. Experimental results indicated the oxygen permeation flux through the BSCF hollow fibre membrane sintered at 1050 ¡ãC was approximately 11.46 mL min?1 cm?2 at 950 ¡ãC when the helium sweep rate was kept at 200 mL min?1. The BSCF hollow fibre membrane showed a stable oxygen permeation flux of 8.60 mL min?1 cm?2 over the investigated period of 120 h at 900 ¡ãC.