The 800 °C isothermal section of the Zn–Si–P ternary system was experimentally determined.
Thermodynamic descriptions of the Zn–P binary system and the Zn–Si–P ternary system were obtained using CALPHAD technique.
ZnSiP2 equilibrates with all the solution phases and intermetallic compounds at 450 °C.