Mo-addition promotes L+(La, Mg)5Ni19 → (La, Mg)2Ni7, particularly for x = 0.15.
The prolonged lifetime induced by Mo is owing to better anti-pulverization ability.
The HRD property for x = 0.15 is enhanced due to change of phase constitution.