Fe0 after magnetization changed surface characteristics and enhanced corrosion.
Pre-magnetized Fe0/PS significantly promoted 2,4-DCP degradation rate and pH suitability.
Possible degradation mechanism by pre-magnetized Fe0/PS was suggested.
Pre-magnetized Fe0/PS was efficient and promising for organics degradation and dechlorination.