Transformation behavior and microstructure feature of large strain ausformed low-temperature bainite in a medium C - Si rich alloy steel

详细信息    查看全文

• 作者：J. Zhao^a ; X. Jia^a ; K. Guo^a ; N.N. Jia^a ; Y.F. Wang^a ; Y.H. Wang^b ; T.S. Wang^a ; ^b ; ^{tswang@ysu.edu.cn}
• 关键词：Medium C - Si rich steel ; Nanostructured bainite ; Ausforming ; Phase transformation kinetics ; Hardness
• 刊名：Materials Science and Engineering: A
• 出版年：2017
• 出版时间：13 January 2017
• 年：2017
• 卷：682
• 期：Complete
• 页码：527-534
• 全文大小：2924 K
• 卷排序：682

文摘

Large-strain ausforming and low-temperature bainite transformation were carried out in a medium C - Si rich alloy steel on a thermomechanical simulator. Then, temperature–time–transformation curves of the bainite transformation after ausforming at different temperatures were obtained by dilatometry. The effects of ausforming on transformation kinetics, microstructure, and hardness of samples were studied. Results show that the entire process of bainite transformation can be accelerated by ausforming. With decreasing ausforming temperature, the transformation rates greatly increased at the initial transformation stage but slightly decreased at the final stage. Compared with non-ausformed sample, not only was the maximum growth rate in the ausformed samples larger, but the maximum growth rate also appeared earlier. In addition, the maximum rate of the ausformed bainite transformation was increased and the time of reaching the maximum rate was shortened with decreasing the ausforming temperature. The effect of ausforming on bainite transformation kinetics depended not only on the ausforming temperature and strain but also on the isothermal transformation temperature. The reduction in transformation time was increased under decreased isothermal transformation temperature. Ausforming refined the bainite plates and increased the fraction of retained austenite formed in the subsequent low-temperature isothermal transformation. Consequently, nanostructured bainite with enhanced hardness was prepared in the medium C - Si rich alloy steel.