Gallium additions stabilized cubic symmetry in garnet-type Li7La3Zr2O12. Ionic conductivity was found to increase with increased density and grain size. Spark plasma sintering method improved the sinterability and grain coarsening. Highest ionic conductivity at room temperature was 5.81 × 10−5 S/cm (Ea = 0.41 eV).