Ni-graphene (Ni-G) composite were synthesized via a one-step electrodeposition.
The maximum content of graphene in the Ni-G composite was 2.82 at%.
Graphene was evenly distributed in the Ni-G composite coatings.
Ni-G/304 SS exhibited a maximum exchange current density was 1.43 mA cm2.
Ni-G/304 SS exhibited a minimum onset overpotential for the HER was 75 mV in 0.1 mol L−1 KOH solution at 298.15 K.