Xanthate-Functional Temperature-Responsive Polymers: Effect on Lower Critical Solution Temperature Behavior and Affinity toward Sulfide Surfaces

详细信息    查看全文

• 作者：Wei Sung Ng ; Elizaveta Forbes ; George V. Franks ; Luke A. Connal
• 刊名：Langmuir
• 出版年：2016
• 出版时间：August 2, 2016
• 年：2016
• 卷：32
• 期：30
• 页码：7443-7451
• 全文大小：481K
• 年卷期：0
• ISSN：1520-5827

文摘

Xanthate-functional polymers represent an exciting opportunity to provide temperature-responsive materials with the ability to selectively attach to specific metals, while also modifying the lower critical solution temperature (LCST) behavior. To investigate this, random copolymers of poly(N-isopropylacrylamide) (PNIPAM) with xanthate incorporations ranging from 2 to 32% were prepared via free radical polymerization. Functionalization with 2% xanthate increased the LCST by 5 °C relative to the same polymer without xanthate. With increasing xanthate composition, the transition temperature increased and the transition range broadened until a critical composition of the hydrophilic xanthate groups (≥18%) where the transition disappeared completely. The adsorption of the polymers at room temperature onto chalcopyrite (CuFeS₂) surfaces increased with xanthate composition, while adsorption onto quartz (SiO₂) was negligible. These findings demonstrate the affinity of these functional smart polymers toward copper iron sulfide relative to quartz surfaces, presumably due to the interactions between xanthate and specific metal centers.