Influences of Surface Roughness of ZnO Electron Transport Layer on the Photovoltaic Performance of Organic Inverted Solar Cells

详细信息    查看全文

• 作者：Zaifei Ma ; Zheng Tang ; Ergang Wang ; Mats R. Andersson ; Olle Ingan盲s ; Fengling Zhang
• 刊名：The Journal of Physical Chemistry C
• 出版年：2012
• 出版时间：November 26, 2012
• 年：2012
• 卷：116
• 期：46
• 页码：24462-24468
• 全文大小：437K
• 年卷期：v.116,no.46(November 26, 2012)
• ISSN：1932-7455

文摘

Here, we demonstrate the correlation between the surface roughness of the ZnO interlayer used as an electron transporting interlayer (ETL) in organic inverted solar cells (ISCs) and the photovoltaic performance of the ISCs. Three different surfaces of the ZnO ETL are studied in ISCs with the polymer poly[2,3-bis-(3-octyloxyphenyl)quinoxaline-5,8-diyl-alt-thiophene-2,5-diyl] (TQ1) mixed with [6,6]-phenyl C71 butyric acid methyl ester (PC₇₁BM) as the active layer. The results obtained from these ISCs show that power conversion efficiency increases from 2.7% to 3.9% when the root-mean-square roughness of the ZnO layer decreases from 48 to 1.9 nm. Moreover, it is found that the short-circuit current density is higher in the ISC based on the smoother ZnO interlayer, with a larger donor/acceptor (D/A) interfacial area in the active layer that facilitates exciton dissociation. The reduced effective interfacial area between the photoactive layer and the ZnO interlayer with decreased ZnO surface roughness leads to an observed improvement in both fill factor and open-circuit voltage, which is ascribed to a reduced concentration of traps at the interface between the ZnO interlayer and the active layer.