High-Performance Transparent Conductive Films Using Rheologically Derived Reduced Graphene Oxide

详细信息    查看全文

• 作者：Seung Yol Jeong ; Sung Hun Kim ; Joong Tark Han ; Hee Jin Jeong ; Sunhye Yang ; Geon-Woong Lee
• 刊名：ACS Nano
• 出版年：2011
• 出版时间：February 22, 2011
• 年：2011
• 卷：5
• 期：2
• 页码：870-878
• 全文大小：1093K
• 年卷期：0
• ISSN：1936-086X

文摘

In this work, we produced large-area graphene oxide (GO) sheets with fewer defects on the basal plane by application of shear stress in solution to obtain high-quality reduced graphene oxide (RGO) sheets without the need for post-annealing processes. This is described as rheologically derived RGO. The large-area GO sheets were generated using a homogenizer in aqueous solution, which induced slippage of the GO in the in-plane direction during the exfoliation process, in contrast with the conventional sonication method. The effects of chemical reduction under mild conditions demonstrated that the formation of structural defects during the exfoliation process affected the RGO properties. In the Raman spectra, the I_D/I_G ratio of the homogenized RGO (HRGO) increased more than that of the sonicated RGO (SRGO) due to the large number of ordered six-fold rings on the basal plane. The enhanced sheet resistance of the HRGO thin film was found to be 2.2 kΩ/sq at 80% transmittance. The effective exfoliation method has great potential for application to high-performance RGO-transparent conducting films.