A Thiophene-Containing Conductive Metallopolymer Using an Fe(II) Bis(terpyridine) Core for Electrochromic Materials

详细信息    查看全文

• 作者：Yawei Liang ; Daniel Strohecker ; Vincent Lynch ; Bradley J. Holliday ; Richard A. Jones
• 刊名：ACS Applied Materials & Interfaces
• 出版年：2016
• 出版时间：December 21, 2016
• 年：2016
• 卷：8
• 期：50
• 页码：34568-34580
• 全文大小：872K
• ISSN：1944-8252

文摘

Three Fe(II) bis(terpyridine)-based complexes with thiophene (Fe(L1)₂), bithiophene (Fe(L2)₂), and 3,4-ethylenedioxythiophene (Fe(L3)₂) side chains were designed and synthesized for the purpose of providing two terminal active sites for electrochemical polymerization. The corresponding metallopolymers (poly-Fe(Ln)₂, n = 2 or 3) were synthesized on indium tin oxide (ITO)-coated glass substrates via oxidative electropolymerization of the thiophene-substituted monomers and characterized using electrochemistry, X-ray photoelectron spectroscopy, UV–vis spectroscopy, and atomic force microscopy. The film poly-Fe(L2)₂ was further studied for electrochromic (EC) color-switching properties and fabricated into a solid-state EC device. Poly-Fe(L2)₂ films exhibit an intense MLCT absorption band at 596 nm (ε = 4.7 × 10⁴ M^–1 cm^–1) in the UV–vis spectra without any applied voltage. Upon application of low potentials (between 1.1 and 0.4 V vs Fc⁺/Fc), the obtained electropolymerized film exhibited great contrast with a change of transmittance percentage (ΔT%) of 40% and a high coloration efficiency of 3823 cm² C^–1 with a switching time of 1 s. The film demonstrates commonplace stability and reversibility with a 10% loss in peak current intensity after 200 cyclic voltammetry cycles and almost no loss in change of transmittance (ΔT%) after 900 potential switches between 1.1 and 0.4 V (vs Fc⁺/Fc) with a time interval of 0.75 s. The electropolymerization of Fe(L2)₂ provides convenient and controllable film fabrication. Electrochromic behavior was also achieved in a solid-state device composed of a poly-Fe(L2)₂ film and a polymer-supported electrolyte sandwiched between two ITO-coated glass electrodes.