Van der Waals Epitaxial Growth of Two-Dimensional Single-Crystalline GaSe Domains on Graphene

详细信息    查看全文

• 作者：Xufan Li ; Leonardo Basile ; Bing Huang ; Cheng Ma ; Jaekwang Lee ; Ivan V. Vlassiouk ; Alexander A. Puretzky ; Ming-Wei Lin ; Mina Yoon ; Miaofang Chi ; Juan C. Idrobo ; Christopher M. Rouleau ; Bobby G. Sumpter ; David B. Geohegan ; Kai Xiao
• 刊名：ACS Nano
• 出版年：2015
• 出版时间：August 25, 2015
• 年：2015
• 卷：9
• 期：8
• 页码：8078-8088
• 全文大小：835K
• ISSN：1936-086X

文摘

Two-dimensional (2D) van der Waals (vdW) heterostructures are a family of artificially structured materials that promise tunable optoelectronic properties for devices with enhanced functionalities. Compared to transferring, direct epitaxy of vdW heterostructures is ideal for clean interlayer interfaces and scalable device fabrication. Here we report the synthesis and preferred orientations of 2D GaSe atomic layers on graphene (Gr) by vdW epitaxy. GaSe crystals are found to nucleate predominantly on random wrinkles or grain boundaries of graphene, share a preferred lattice orientation with underlying graphene, and grow into large (tens of micrometers) irregularly shaped, single-crystalline domains. The domains are found to propagate with triangular edges that merge into the large single crystals during growth. Electron diffraction reveals that approximately 50% of the GaSe domains are oriented with a 10.5 卤 0.3掳 interlayer rotation with respect to the underlying graphene. Theoretical investigations of interlayer energetics reveal that a 10.9掳 interlayer rotation is the most energetically preferred vdW heterostructure. In addition, strong charge transfer in these GaSe/Gr vdW heterostructures is predicted, which agrees with the observed enhancement in the Raman E²_1g band of monolayer GaSe and highly quenched photoluminescence compared to GaSe/SiO₂. Despite the very large lattice mismatch of GaSe/Gr through vdW epitaxy, the predominant orientation control and convergent formation of large single-crystal flakes demonstrated here is promising for the scalable synthesis of large-area vdW heterostructures for the development of new optical and optoelectronic devices.