参考文献:1.Jain, I., Lai, C., and Jain, A., Int. J. Hydrogen. Energy, 2010, vol. 35, p. 5133.View Article 2.Khaldi, C., Mathlouthi, H., and Lamloumi, J., J. Alloys. Compd., 2009, vol. 469, p. 464.View Article 3.Wang, Y., Zhao, M., Li, S., and Wang, L., Electrochim. Acta, 2008, vol. 537, p. 831. 4.Pan, H.G., Ma, J.X., Wang, C.S., Chen, C.P., and Wang, Q.D., Electrochim. Acta, 1999, vol. 44, p. 3977.View Article 5.Zhang, P., Wei, X., Liu, Y., Zhu, J., Zhang, Z., and Zhao, T., J. Alloys. Compd., 2005, vol. 399, p. 270.View Article 6.Durairajan, A., Haran, B.S., White, R.E., and Popov, B.N., J. Power. Sources, 2000, vol. 87, p. 84.View Article 7.Giza, K., Iwasieczko, W., and Pavlyuk, V.V., J. Alloys. Compod., 2007, vol. 429, p. 352.View Article 8.Chai, Y.J. and Wang, N., Rare. Metal. Mat. Eng., 2010, vol. 39, suppl. 1, p. 24. 9.Kohno, T., Yoshida, H., Kawashima, F., Inaba, T., Sakai, I., Yamamoto, M., and Kanda, M., J. Alloys. Compd., 2000, vol. 311, p. L5.View Article 10.Spassov, T., Lyubenova, L., K枚ster, U., and Bar贸, M., Mater. Sci. Eng. A, 2004, vol. 375, p. 794.View Article 11.Khaldi, C., Boussami, S., Rejeb, B.B., Mathlouthi, H., and Lamloumi, J., Mater. Sci. Eng. B, 2010, vol. 175, p. 22.View Article 12.Lu, D.S., Li, W.S., Hu, S.J., Xiao, F.M., and Tang, R.H., Int. J. Hydrogen. Energy, 2006, vol. 31, p. 678.View Article 13.Ming, Au., Mater. Sci., 2005, vol. 117, p. 37. 14.Erbacher, J.K., J. Power. Sources, 1999, vol. 80, p. 265.View Article 15.Nelson, R.F., J. Power. Sources, 2000, vol. 9, p. 12. 16.Zhang, X.B., Chai, Y.J., Yin, W.Y., and Zhao, M.S., J. Rare. Earth., 2003, vol. 21, p. 162. 17.Okumura, M., Ikado, A., Saito, Y., Aoki, H., Miura, T., and Kawakami, Y., Int. J. Hydrogen. Energy, 2012, vol. 37, p. 10715.View Article 18.Zou, J.X., Zeng, X.Q., Ying, Y.J., Chen, X., Guo, H., Zhou, S., and Ding, W.J., Int. J. Hydrogen. Energy, 2013, vol. 38, p. 2337.View Article 19.Qin, F., Guo, L.H., Chen, J.P., and Chen, Z.J., Int. J. Hydrogen. Energy, 2008, vol. 33, p. 707.View Article 20.Guo, P.P., Lin, Y.F., Zhao, H.H., Guo, S.H., and Zhao, D.L., J. Rare. Earths., 2011, vol. 29, p. 574.View Article 21.Chu, H.L., Qiu, S.J., Sun, L.X., Zhang, Y, Xu, F., Jiang, T., Li, W.X., Zhu, M., and Hu, W.Y., Electrochim. Acta, 2007, vol. 52, p. 6700.View Article
作者单位:P. Lv (1) Z.-M. Wang (1) J.-Q. Deng (1)
1. School of Materials Science & Engineering, Guilin University of Electronic Technology, No. 1, Jinji Road, Guilin, 541004, China
刊物类别:Chemistry and Materials Science
刊物主题:Chemistry Electrochemistry Physical Chemistry Russian Library of Science
出版者:MAIK Nauka/Interperiodica distributed exclusively by Springer Science+Business Media LLC.
ISSN:1608-3342
文摘
A series of experiments were performed to investigate the effect of the temperature on electrode performance of the as-cast La0.7Mg0.3(NiMnCo)3.5 alloy. XRD and SEM show that La0.7Mg0.3(NiMnCo)3.5 alloy has LaNi5 and La2Ni7 phase. The activation curves show that the as-cast La0.7Mg0.3(NiMnCo)3.5 alloy electrode can be activated in three times and the maximum discharge capacity is 358.74 mA h/g at 273 K. With increasing the temperature, the cyclic stability of the alloy electrode decreases obviously. And the capacity retention decreases from 96.14 to 63.53% when the temperature increases from 238 to 303 K. It also can be seen that the as-cast La0.7Mg0.3(NiMnCo)3.5 alloy electrode has the best self-discharge ability at 238 K and the best high-rate discharge ability at 273 K.