参考文献:1. Marcilla, A., Garia, S., Garcia-Quesdad, J. C. (2004) J. Anal. Appl. Pyrol. 7: pp. 457 CrossRef 2. Latini, G., Felice, C.D., Verrotti, A. (2004) Reprod Toxicol. 19: pp. 27 CrossRef 3. Ltini, G. (2000) Biology of Neonat 78: pp. 269 CrossRef 4. Li, J. H., Ko, Y. C. (2012) Kaohsiung J. Med. Sci. 28: pp. 17 CrossRef 5. Chen, Y. H., Fu, S. H., Huang, J. K. (2013) J. Food Drug. Anal. 21: pp. 242 CrossRef 6. Hakkarainen, M. (2008) Adv. Polym. Sci. 211: pp. 159 CrossRef 7. Chiu, F. C., Min, K. (2000) Polym. Int. 49: pp. 223 CrossRef 8. Shah, B. L., Shertukde, V.V. J. (2003) Appl. Polym. Sci. 90: pp. 3278 CrossRef 9. Soonja, C., Yoon-Jong, C. (1995) Polymer 36: pp. 4977 CrossRef 10. Sander, M. M., Nicolau, A., Guzatto, R. (2012) Polym Test 31: pp. 1077 CrossRef 11. Silva, M.A.D., Vieira, M. G. A., Macumoto, A. C. G. (2011) Polym. Test 30: pp. 478 CrossRef 12. Li, Y., Wang, C.M., Wang, G. J. (2008) J. Wuhan Univ. Technol. 2: pp. 100 CrossRef 13. Wu, Y. M., Xie, Q.W., Gao, C. H. (2013) Polym. Eng. Sci.. 14. Djordjevic, I., Choudhury, N.R., Dutta, N.K. (2009) Polymer 50: pp. 1682 CrossRef 15. Sathiskumar, P. S., Madras, G. (2011) Polym. Degrad. Stabil. 96: pp. 1695 CrossRef 16. Edlund, U., Albertsson, A.C. (2002) Adv. Polym. Sci. 157: pp. 67 CrossRef 17. Vieira, M.G. A., Silva, M. A., Santos, L.O. (2011) Eur. Polym. J. 47: pp. 254 CrossRef 18. Espinosa, L. M., Meier, M. A. R. (2011) Eur. Polym. J. 47: pp. 837 CrossRef 19. Sudesh, K., Abe, H., Doi, Y. (2000) Prog. Polym. Sci. 25: pp. 1503 CrossRef 20. Isa, M.T., Ahmed, A. S., Aderemi, B.O. (2013) Composites: Part B 53: pp. 217 CrossRef 21. Salimon, J., Salih, N., Yousif, E. (2012) Arab. J. Chem. 5: pp. 135 CrossRef 22. Bordes, P., Pollet, E., Avérous, L. (2009) Prog. Polym. Sci. 34: pp. 125 CrossRef 23. Sharma, V., Kundu, P. P. (2006) Prog. Polym. Sci. 31: pp. 983 CrossRef 24. Chua, S.C., Xu, X.B., Guo, Z. (2012) Process Biochem. 47: pp. 1439 CrossRef
刊物类别:Chemistry and Materials Science
刊物主题:Chemistry Industrial Chemistry and Chemical Engineering Catalysis Materials Science Biotechnology
出版者:Springer New York
ISSN:1975-7220
文摘
A unique biobased polyester poly(succinic acid-glyceryl monooleate) (PSAGMO) was synthesized and characterized from succinic acid (SA) and glyceryl monooleate (GMO). The polyester was characterized by gel permeation chromatography (GPC), Fourier transform infrared spectroscopy (FTIR) and nuclear magnetic response spectroscopy (NMR). The polyester was used as the plasticizer of poly (vinyl chloride) (PVC). The mechanical properties and the thermodynamic properties of the blends were characterized. The TG-DTA data indicated that the thermal degradation temperature (T d ) of PVC blends plasticized with PSAGMO could increase from 249.3 °C to 255.6 °C. The DMA showed that the glass transition temperature (Tg) of the PVC blends decreased from 49.5 °C to 35 °C. The mechanical properties indicated that the PSAGMO could decrease the tensile strength and increase the elongation at break of the PVC blends. This study may lead to the development of new type of PVC plasticizer based on renewable resource.