Synthesis of low polydisperse isotactic poly(N-isopropylacrylamide)s in environment-friendly and less toxic methanol-water mixtures by RAFT polymerization
参考文献:1.Matyjaszewski K 1998 Ed. ACS Symp. Ser. 685 2.Matyjaszewski K 2000 Ed. ACS Symp. Ser. 768 3.Matyjaszewski K and Xia J 2001 Chem. Rev. 101 2921CrossRef 4.Kamigaito M, Ando T and Sawamoto M 2001 Chem. Rev. 101 3689CrossRef 5.Chiefari J, Chong Y K, Ercole F, Krstina J, Jeffery J, Le T P T, Mayadunne R T A, Meijs G F, Moad C L, Moad G, Rizzardo E and Thang S H 1998 Macromolecules 31 5559CrossRef 6.Goto A, Sato K, Tsujii Y, Fukuda T, Moad G, Rizzardo E and Thang S H 2001 Macromolecules 34 402CrossRef 7.Soloman D H and Rizzardo E 1986 US Patent 4 (581) 429 8.Georges M K, Veregin R P N, Kazmaier K M and Hamer G K 1993 Macromolecules 26 2987CrossRef 9.Schulte T, Siegenthaler K O, Luftmann H, Letzel M and Studer A 2005 Macromolecules 38 6833CrossRef 10.Xia Y, Burke N A D and Stöver H D H 2006 Macromolecules 39 2275CrossRef 11.Xia Y, Yin X, Burke N A D and Stöver H D H 2006 Macromolecules 38 5937CrossRef 12.Yamashita K, Yamamoto K and J-i K. 2013 Polymer 54 1775CrossRef 13.Ye J and Narain R 2009 J. Phys. Chem. B 113 676CrossRef 14.Xu J, Ye J and Liu S 2007 Macromolecules 40 9103CrossRef 15.Masci G, Giacomelli L and Crescenzi V 2004 Macromol. Rapid Commun. 25 559CrossRef 16.Convertine A J, Ayres N, Scales C W, Lowe A B and McCormick C L 2004 Biomacromolecules 5 1177CrossRef 17.Schilli C, Lanzendörfer M G and Müller A H E 2002 Macromolecules 35 6819CrossRef 18.Ganachaud F, Monteiro M J, Gilbert R G, Dourges M -A, Thang S H and Rizzardo E 2000 Macromolecules 33 6738CrossRef 19.Bai W, Zhang L, Bai R and Zhang G 2008 Macromol. Rapid Commun. 29 562CrossRef 20.Wang X, Li S, Su Y, Hou F and Zhang W 2013 J. Polym. Sci., Part A: Polym. Chem. 51 2188CrossRef 21.Ray B, Isobe Y, Morioka K, Habaue S, Okamoto Y, Kamigaito M and Sawamoto M 2003 Macromolecules 36 543CrossRef 22.Ray B, Isobe Y, Matsumoto K, Habaue S, Okamoto Y, Kamigaito M and Sawamoto M 2004 Macromolecules 37 1702CrossRef 23.Das S, Samanta S, Chatterjee D P and Nandi A K 2013 J. Polym. Sci. Part A: Polym. Chem. 51 1417CrossRef 24.Das S, Chatterjee D P, Samanta S and Nandi A K 2013 RSC Adv. 3 17540CrossRef 25.Ray B, Okamoto Y, Kamigaito M, Sawamoto M, Seno K, Kanaoka S and Aoshima S 2005 Polym. J. 37 234CrossRef 26.Heskins M and Guillet J E 1968 J. Macromol. Sci. Chem. A2 1441CrossRef 27.Fujishige S, Kubota K and Ando I 1989 J. Phys. Chem. 93 3311CrossRef 28.Tong Z, Zeng F, Zheng X and Sato T 1999 Macromolecules 32 4488CrossRef 29.de Azevedo R G, Rebelo L P N, Ramos A M, Szydlowski J, de Sousa H C and Klein J 2001 Fluid Phase Equilib. 185 189CrossRef 30.Biswas C S, Vishwakarma N K, Patel V K, Mishra A K, Saha S and Ray B 2012 Langmuir 28 7014CrossRef 31.Quinin J F, Rizzardo E and Davis T P 2001 Chem. Commun. 1044 32.Biswas C S, Patel V K, Vishwakarma N K, Mishra A K, Saha S and Ray B 2010 Langmuir 26 6775CrossRef 33.Biswas C S, Mitra K, Singh S, Ramesh K, Misra N, Maiti B, Panda A K, Maiti P, Kamigaito M, Okamoto Y and Ray B 2015 Colloid Polym. Sci. 293 1749CrossRef
1. Department of Chemistry, Faculty of Science, Banaras Hindu University, Varanasi, 221005, India 2. Nanshan District Key Lab for Biopolymers and Safety Evaluation, College of Materials Science and Engineering & Optoelectronic Engineering Postdoctoral Center, Shenzhen University, 518060, Shenzhen, China
刊物类别:Chemistry and Materials Science
刊物主题:Chemistry Chemistry
出版者:Springer India
ISSN:0973-7103
文摘
Poly(N-isopropylacrylamide)s (PNIPAM) with low polydispersity and different isotacticity have been synthesized successfully in different compositions of environment-friendly and less toxic methanol-water mixtures by RAFT polymerization in the presence of 0.1 M Yttrium trifluoromethanesulfonate [Y(OTf) 3]. The reactions were successful with high yield in the solvent compositions having mole-fraction of methanol (x m) at or above 0.31. Molecular weights were found to be in between 2.78 × 10 4 – 5.7 × 10 4 and polydispersity index (M w/ M n= 1.11 – 1.37) was close to unity. Isotacticity [meso diad (m), %] of the polymers increased from 55 to 86% with the increase in the x m value from 0.31 to 1.0. The lower critical solution temperature (LCST) of the formed PNIPAMs in water decreased with the increase in their isotacticity.