Evaluation of dynamic recrystallization behaviors in hot-extruded AA5083 through hot torsion tests

详细信息    查看全文

• 作者：Kwang-Tae Son ; Ji-Woon Lee ; Taek-Kyun Jung…
• 关键词：alloys ; hot working ; recrystallization ; hot torsion test ; optical microscopy
• 刊名：Metals and Materials International
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：23
• 期：1
• 页码：68-75
• 全文大小：
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Metallic Materials; Operating Procedures, Materials Treatment; Magnetism, Magnetic Materials; Engineering Thermodynamics, Heat and Mass Transfer; Characterization and Evaluation of Materials; Continuu
• 出版者：The Korean Institute of Metals and Materials
• ISSN：2005-4149
• 卷排序：23

文摘

Hot torsion tests were carried out to evaluate the dynamic recrystallization (DRX) behaviors of hot-extruded AA5083 at various deformation conditions. Flow curves showed the peak followed by the flow softening to the steady-state or to the failure strain, indicating that the DRX occurred during deformation. The peak stress increased as the temperature decreased and the strain rate increased. Constitutive relationship and Zener-Hollomon (Z) parameter were used to evaluate the DRX characteristics. Peak and steady-state stresses were generalized by the dimensionless parameter, Z/A, to reveal the DRX mechanism. The empirical relationship of the DRXed grain size with the deformation conditions was established, and decreased with increasing Z parameter. The relationship for the fraction of DRXed grains was established as a function of the effective strain at given deformation conditions from the experimental data. The Avrami relationship based on micro-hardness measurement was used to describe the DRX kinetics, and was fitted well with the observed DRX fraction.