Development of Strong η Fiber Recrystallization Texture in Rolled Fe81Ga19 Thin Sheet

详细信息    查看全文

• 作者：Zhenghua He (1)
  Yuhui Sha (1)
  Fang Zhang (1)
  Feifei Lin (1)
  Liang Zuo (1)
  
• 刊名：Metallurgical and Materials Transactions A
• 出版年：2014
• 出版时间：January 2014
• 年：2014
• 卷：45
• 期：1
• 页码：129-133
• 全文大小：
• 作者单位：Zhenghua He (1)
  Yuhui Sha (1)
  Fang Zhang (1)
  Feifei Lin (1)
  Liang Zuo (1)
  
  1. Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), Northeastern University, Shenyang, 110819, P.R. China
  
• ISSN：1543-1940

文摘

The 0.50-mm-thick Fe81Ga19 sheets were produced by rolling procedure, and texture evolution was investigated using macro- and microtexture analyses. The recrystallization texture dominated with strong η fiber (〈001〉//RD) was successfully obtained through sheet thickness by primary recrystallization annealing. The η fiber development can be attributed to the advantage in both grain number and grain size derived from the specially applied rolling process.