Experimental study for rubber pad forming process of AZ31 magnesium alloy sheets at warm temperature

详细信息    查看全文

• 作者：Junrui Xu ; Yingqi Zhou ; Junjia Cui…
• 关键词：AZ31 sheet ; Drawing ; Rubber pad forming ; Warm temperature
• 刊名：The International Journal of Advanced Manufacturing Technology
• 出版年：2017
• 出版时间：March 2017
• 年：2017
• 卷：89
• 期：1-4
• 页码：1079-1087
• 全文大小：
• 刊物类别：Engineering
• 刊物主题：Industrial and Production Engineering; Media Management; Mechanical Engineering; Computer-Aided Engineering (CAD, CAE) and Design;
• 出版者：Springer London
• ISSN：1433-3015
• 卷排序：89

文摘

In this paper, forming behavior of AZ31 sheet in rubber pad forming with warm temperature was investigated by experimental method. Rubber pad is always considered as it is temperature resistant. However, some types of rubbers can endure warm temperature, such as polyurethane for 120 °C and silica gel for 250 °C. Thus, forming for coupling with effects of temperature and flexible of rubber pad is proposed in this paper. The forming process of AZ31 sheet experienced bulging first and then gradually contacting with die, which was different from conventional forming. Fracture presented flat at room temperature and fracture became dentation obviously at 100 °C. When the temperature elevated to 200 °C, the fracture does not occur but the polyurethane was melted. The AZ31 sheet could fill the die successfully with silica gel as rubber pad at 200 °C. The effects of different load velocity for forming of AZ31 sheet were investigated. Thickness increased at bottom of deformed part, due to pressure stress acted from surrounding area. The thickness deceased at the bottom corner. Microstructure of deformed AZ31 sheet was also analyzed. It was indicated that dynamic recrystallization and twinning deformation mechanics were activated which had positive influence for improving formability of AZ31 sheet.