文摘
Series of novel low-firing microwave dielectric ceramics with the composition of Li1+2x Mg4?em class="a-plus-plus">x V3O12 (?.2?≤?em class="a-plus-plus">x?≤?.1) were prepared by a solid-state reaction process. The crystal structure, sintering behavior and microwave dielectric properties of ceramics were investigated using X-ray diffraction, scanning electron microscopy and dielectric measurement. As x increased from ?.2 to 0.1, the optimized sintering temperature was reduced from 880 to 700?°C, the quality factors (Q?×?f) were effectively enhanced from 21,000 to 33,200?GHz. A good combined microwave dielectric properties with εr?=?12.1, Q?×?f?=?21,800?GHz, τ f ?=?1.8?ppm/°C were obtained for x?=??.1.