Method of Evaluating Delayed Fracture Susceptibility of Tempered Martensitic Steel Showing Quasi-Cleavage Fracture
详细信息 查看全文
- 作者：Yu Matsumoto ; Kenichi Takai
- 刊名：Metallurgical and Materials Transactions A
- 出版年：2017
- 出版时间：February 2017
- 年：2017
- 卷：48
- 期：2
- 页码：666-677
- 全文大小：1997KB
- 刊物类别：Chemistry and Materials Science
- 刊物主题：Metallic Materials; Characterization and Evaluation of Materials; Structural Materials; Surfaces and Interfaces, Thin Films; Nanotechnology;
- 出版者：Springer US
- ISSN：1543-1940
- 卷排序：48
文摘
The difference in the hydrogen charging methods, immersion in a NH4SCN aqueous solution, and cathodic electrolysis in a NaOH aqueous solution, did not affect the hydrogen state present in the steel, but it did affect the surface state of the specimens through corrosion, causing fracture strength to fluctuate in tensile testes. As for stress application method, the fracture strength at lower crosshead speeds in tensile tests was consistent with that found for hydrogen precharging prior to stress application in CLTs as long as hydrogen charging was conducted by cathodic electrolysis. However, the fracture strength obtained with concurrent hydrogen charging without precharging prior to stress application in CLTs was higher than that with hydrogen precharging prior to stress application in CLTs regardless of the same hydrogen content. In other words, delayed fracture susceptibility was affected by the order of hydrogen charging and stress application for quasi-cleavage fracture associated with local plastic deformation, i.e., dislocation motion. Therefore, by taking into account the cathodic electrolysis in the NaOH solution, the low crosshead speed and the order of hydrogen charging and stress application, the fracture strength in CLTs, and tensile tests coincided with respect to quasi-cleavage fracture even though the stress application methods were different.