刊物主题:Chemistry Optical and Electronic Materials Ceramics,Glass,Composites,Natural Materials Characterization and Evaluation Materials Electrochemistry Crystallography
出版者:Springer Netherlands
ISSN:1573-8663
文摘
We have studied glass formable region in the Y2O3-CaO-Al2O3 system. An optimal composition for the amorphous phase formation was found in the pseudo-eutectic 12CaO?7Al2O3-CaYAlO4 system. An amorphous bulk plate of 10 × 25 × 1.8 mm was successfully fabricated using a simple molding technique. The fabricated glass plate showed an IR absorption edge at around 5.6 μm. The crystallization of the glass sample was observed above 890°C by an X-ray diffraction (XRD) and Thermogravimetry and Differential thermal analysis (TG-DTA).