摘要
采用连续预氧化、碳化制备方法,对PAN纤维低温碳化阶段不同温度条件下的纤维进行DSC、线密度和元素分析等表征分析测试,研究其低温碳化过程中组分的演变规律。结果表明:预氧丝由室温进入低温炉,大约350℃时会发生瞬时热收缩,造成线密度由950g/km增加至990g/km,增加了4. 2%。在450℃时,发生热分解反应,生成丙烯腈二聚体、三聚体系列物质和小分子气体,失重30%。随着纤维逐步加热,N,H和O逐渐脱除,经碳化工序最高温度为700℃处理后纤维碳含量增加至70%。
The continuous Pre-oxidation and carbonization methods were used to characterize the PAN fibers at different temperatures during low-temperature carbonization by DSC,linear density and elemental analysis. The results show that the instantaneous heat shrinkage occurs when the pre-oxidized wire enters the cryogenic furnace from room temperature to about 350℃,resulting in linear density increased by 950 g/km to 990 g/km,increased by 4. 2%. At 450℃,thermal decomposition reaction takes place,resulting in the formation of acrylonitrile dimers,trimers and small molecule gas,and the weightlessness is aggravated 30%. As the fibers were heated gradually,N,H and O were removed,and the carbon content of the fibers increased to 70% after carbonization at 700℃.
引文
[1]童元建,王统帅,王小谦,等.PAN基碳纤维制备过程中的组成演变[J].化工新型材料,2011,39(4):97-99.
[2]高爱君,罗莎,张佐光,等.PAN纤维在特征碳化温度下的反应特性[J].化工新型材料,2015(9):110-112.
[3]王统帅,童元建,罗莎,等.低温碳化过程PAN氧化纤维骨架结构转变[J].材料科学与工艺,2011,19(6):133-137.
[4]刘化虎,吴相升,宋会青.聚丙烯腈纤维的氧化碳化工艺[J].安徽化工,2016,42(3):38-39.
[5]许东,王华,彭卫东,等.PAN基预氧化纤维碳化过程中结构与性能变化[J].合成纤维,2016,45(11).
[6]王成国,朱波.聚丙烯腈基碳纤维[M].科学出版社,2011.