改性双氰胺研究进展
|
摘要
针对双氰胺固化温度较高、在环氧树脂中分散不均等缺点,综述了物理和化学改性方法对双氰胺固化反应活性和储存性能的影响,结合双氰胺的固化机理,分析了双氰胺的改性原理,展望了其未来的发展方向。
In order to overcome the disadvantages of dicyandiamide, such as high curing temperature, poor dispersion in epoxy resin and so on, the effects of chemical and physical modification methods on the curing activity and storage performance of dicyandiamide are reviewed. The curing mechanism of dicyandiamide, chemical and physical modification methods are summarized in this paper. The future development of dicyandiamide is also prospected.
In order to overcome the disadvantages of dicyandiamide, such as high curing temperature, poor dispersion in epoxy resin and so on, the effects of chemical and physical modification methods on the curing activity and storage performance of dicyandiamide are reviewed. The curing mechanism of dicyandiamide, chemical and physical modification methods are summarized in this paper. The future development of dicyandiamide is also prospected.
引文
[1] LIU X D,ATSUSHI S,TAKESHI E.Efficient accelerating effect of carbonyl dfimidazole on epoxy-dicyandiamide curing system[J].Journal of Polymer Science Part A:Polymer Chemistry, 2011,49(1):250-256.
[2]王权,史铁钧,虞伕,等.新型潜伏性固化剂的合成及性能[J].化工学报,2014,65(9):3712-3717.
[3]陈平,刘立柱.节基二甲胺/双氰胺/环氧树脂体系固化反应和固化物性能的研究[J].纤维复合材料,1997,5(3):5-12.
[4]焦剑,蓝立文,宁荣昌.改性双氰胺固化环氧树脂的研究[J].西北工业大学学报,1999,17(4):619-623.
[5]谷晓昱,张军营.用FT-IR研究双氰胺固化环氧树脂的反应机理[J].高分子材料科学与工程,2006,22(5):182-184.
[6]盘文辉.原位红外法研究双氰胺固化环氧树脂[C]//第十五届中国覆铜板技术·市场研讨会暨覆铜板产业协同创新国际论坛论文集,2014.
[7]吴秉灵.双氰胺衍生物—环氧树脂固化体系的研究[J].绝缘材料通讯,1990,155(1):9-12.
[8] LEBEL 0, MARIS T, DUVAL H, et al. A practical guide to arylbiguanides-Synthesis and structural characterization[J]. Revue Canadienne De Chimie,2005,83(6-7):615-625.
[9]史俊,崔进,李恒娟.一种新型改性双氰胺固化剂的合成及性能研究[J].中国胶黏剂,2006,15(10):15-17.
[10]杨宗溢,何劲,陈连喜,等.间甲苯胺改性双氰胺的合成及固化性能研究[J].湖北工业大学学报,2006,21(5):16-18.
[11]程秀莲,孙丰雅,霸书红.邻甲基苯胺改性双氰胺环氧固化剂的合成及性能研究[J].粘接,2014,35(12):60-63.
[12]陈连喜,张惠玲,刘全文,等.间甲苯胺改性双氰胺衍生物的合成[J].武汉理工大学学报,2005,27(8):11-13.
[13]陈连喜,张惠玲,刘全文,等.芳香胺改性双氰胺固化环氧树脂反应动力学研究[J].热固性树脂,2006,21(6):11-13.
[14]冯利邦,王玉龙,郝相忠,等.新型改性双氰胺固化剂对环氧树脂的固化行为研究[J].材料导报,2012,26(14):59-62.
[15]王永超,林树东,涂园园,等.一种环氧树脂潜伏性固化剂二苯基双胍的合成与性能[J].精细化工,2016,33(2):224-230.
[16]陈秀宇,陈玉成,林谦.单组分环氧胶固化剂及促进剂的改性研究.应用化工,2008,38(2):146-148.
[17]黄圣梅,梁红波,熊磊.改性双氰胺衍生物环氧固化剂的制备及性能研究[J].中国胶黏剂,2009,18(12):5-9.
[18]尚明屹.液化双氰胺环氧树脂固化剂的制备与研究[D].厦门:厦门大学,2013.
[19]唐囡,杨又华,邓静伟,等.双酚A型酚醛树脂改性双氰胺固化环氧树脂行为的研究[J].表面技术,2014,43(6):144-148.
[20]周建萍,曾庆煜,曹万荣,等.甲醛改性双氰胺水性环氧树脂潜伏性固化剂的研制[J].涂料工业,2010,40(12):13-16.
[21]程秀莲,郭小伟,杨艳玲.苯甲醛改性双氰胺环氧固化剂的研究[J].粘接,2015,36(3):43-46.
[22]李伟,程秀莲,张致豪,等.糠醛改性双氰胺的制备及性能研究[J].粘接,2016,37(10):42-45.
[23]吴忠喜,王锋,涂伟萍.潜伏性环氧树脂胶黏剂用液态改性双氰胺固化剂的研究[J].中国胶黏剂,2013,22(10):7-10.
[24] PEARCE P J,ENNIS B C. Aging and performance of structural film adhesives. IV. A modified epoxy with improved ambient temperature shelf life[J]. Journal of Applied Polymer Science, 1993,47(8):1401-1409.
[25] GUTHNER T, HAMMER B. Curing of epoxy resins with dicyandiamide and urones[J]. Journal of Applied Polymer Science,1993,50(8):1453-1459..
[26] LALIBERTE B R, BORNSTEIN J, SACHER R E.Cure behavior of an epoxy resin-dicyandiamide system accelerated by monuron[J]. Industrial&Engineering Chemistry Product Research and Development. 1983,22(2):261-262..
[27]张保龙,石可瑜,由英才.取代脲促进环氧树脂/双氰胺固化体系反应机理[J].应用化学,1998,14(4):95-97..
[28]黄吉甫,梁贤,张保龙,等.脲衍生物对环氧树脂/双氰双胺固化体系潜伏性促进作用研究[J].高分子学报,1989,99(3):329-336.
[29]洪旭辉,华幼卿.3221中温固化环氧树脂体系的固化反应[J].高分子材料科学与工程,2006,22(5):58-61.
[30]陶永忠.环氧树脂潜伏性固化剂[P].CN03115860,2004.
[31]郑国兵,郑亚萍,吴非.脲衍生物对环氧树脂/双氰胺体系促进作用的研究[J].中国塑料,2013,27(3):47-52.
[32]娄春华,马立群,王雅珍.双氰胺固化环氧树脂促进剂的研制[J].精细石油化工,2009,26(4):29-32.
[33]李彦玲,高堂铃,高洁,等.苯基缩水甘油醚改性2-甲基咪哩促进剂的研究[J].化学与黏合,2016,38(6):417-419.
[34]何尚锦,石可瑜,张珍坤,等.扩链脲改性环氧树脂E-51/双氰双胺(dicy)体系的固化行为[J].应用化学,2001,18(11):857-860.
[35]李瑞珍.新型咪唑类环氧固化促进剂[J].热固性树脂,1994,33(1):34-37.
[36]程秀莲,杨莹,刘运斌,等.酒石酸改性咪唑制备工艺及性能研究[J].粘接,2016,37(11):35-38.
[37]陈平.苄基二甲胺/双氰胺/环氧树脂体系固化物性能的研究[J].工程塑料应用,1992,10(1):11-14.
[38]高玉,余云照,赵彤.双氰胺与间苯二酚在环氧树脂固化中协同作用的研究[C].第十次全国环氧树脂应用技术学术交流会论文集,2003.
[39]唐卿珂,黄琴琴.溶剂对环氧树脂/双氰胺体系固化反应及覆铜板性能的影响[C].第九届全国印制电路学术年会论文集,2012.
[2]王权,史铁钧,虞伕,等.新型潜伏性固化剂的合成及性能[J].化工学报,2014,65(9):3712-3717.
[3]陈平,刘立柱.节基二甲胺/双氰胺/环氧树脂体系固化反应和固化物性能的研究[J].纤维复合材料,1997,5(3):5-12.
[4]焦剑,蓝立文,宁荣昌.改性双氰胺固化环氧树脂的研究[J].西北工业大学学报,1999,17(4):619-623.
[5]谷晓昱,张军营.用FT-IR研究双氰胺固化环氧树脂的反应机理[J].高分子材料科学与工程,2006,22(5):182-184.
[6]盘文辉.原位红外法研究双氰胺固化环氧树脂[C]//第十五届中国覆铜板技术·市场研讨会暨覆铜板产业协同创新国际论坛论文集,2014.
[7]吴秉灵.双氰胺衍生物—环氧树脂固化体系的研究[J].绝缘材料通讯,1990,155(1):9-12.
[8] LEBEL 0, MARIS T, DUVAL H, et al. A practical guide to arylbiguanides-Synthesis and structural characterization[J]. Revue Canadienne De Chimie,2005,83(6-7):615-625.
[9]史俊,崔进,李恒娟.一种新型改性双氰胺固化剂的合成及性能研究[J].中国胶黏剂,2006,15(10):15-17.
[10]杨宗溢,何劲,陈连喜,等.间甲苯胺改性双氰胺的合成及固化性能研究[J].湖北工业大学学报,2006,21(5):16-18.
[11]程秀莲,孙丰雅,霸书红.邻甲基苯胺改性双氰胺环氧固化剂的合成及性能研究[J].粘接,2014,35(12):60-63.
[12]陈连喜,张惠玲,刘全文,等.间甲苯胺改性双氰胺衍生物的合成[J].武汉理工大学学报,2005,27(8):11-13.
[13]陈连喜,张惠玲,刘全文,等.芳香胺改性双氰胺固化环氧树脂反应动力学研究[J].热固性树脂,2006,21(6):11-13.
[14]冯利邦,王玉龙,郝相忠,等.新型改性双氰胺固化剂对环氧树脂的固化行为研究[J].材料导报,2012,26(14):59-62.
[15]王永超,林树东,涂园园,等.一种环氧树脂潜伏性固化剂二苯基双胍的合成与性能[J].精细化工,2016,33(2):224-230.
[16]陈秀宇,陈玉成,林谦.单组分环氧胶固化剂及促进剂的改性研究.应用化工,2008,38(2):146-148.
[17]黄圣梅,梁红波,熊磊.改性双氰胺衍生物环氧固化剂的制备及性能研究[J].中国胶黏剂,2009,18(12):5-9.
[18]尚明屹.液化双氰胺环氧树脂固化剂的制备与研究[D].厦门:厦门大学,2013.
[19]唐囡,杨又华,邓静伟,等.双酚A型酚醛树脂改性双氰胺固化环氧树脂行为的研究[J].表面技术,2014,43(6):144-148.
[20]周建萍,曾庆煜,曹万荣,等.甲醛改性双氰胺水性环氧树脂潜伏性固化剂的研制[J].涂料工业,2010,40(12):13-16.
[21]程秀莲,郭小伟,杨艳玲.苯甲醛改性双氰胺环氧固化剂的研究[J].粘接,2015,36(3):43-46.
[22]李伟,程秀莲,张致豪,等.糠醛改性双氰胺的制备及性能研究[J].粘接,2016,37(10):42-45.
[23]吴忠喜,王锋,涂伟萍.潜伏性环氧树脂胶黏剂用液态改性双氰胺固化剂的研究[J].中国胶黏剂,2013,22(10):7-10.
[24] PEARCE P J,ENNIS B C. Aging and performance of structural film adhesives. IV. A modified epoxy with improved ambient temperature shelf life[J]. Journal of Applied Polymer Science, 1993,47(8):1401-1409.
[25] GUTHNER T, HAMMER B. Curing of epoxy resins with dicyandiamide and urones[J]. Journal of Applied Polymer Science,1993,50(8):1453-1459..
[26] LALIBERTE B R, BORNSTEIN J, SACHER R E.Cure behavior of an epoxy resin-dicyandiamide system accelerated by monuron[J]. Industrial&Engineering Chemistry Product Research and Development. 1983,22(2):261-262..
[27]张保龙,石可瑜,由英才.取代脲促进环氧树脂/双氰胺固化体系反应机理[J].应用化学,1998,14(4):95-97..
[28]黄吉甫,梁贤,张保龙,等.脲衍生物对环氧树脂/双氰双胺固化体系潜伏性促进作用研究[J].高分子学报,1989,99(3):329-336.
[29]洪旭辉,华幼卿.3221中温固化环氧树脂体系的固化反应[J].高分子材料科学与工程,2006,22(5):58-61.
[30]陶永忠.环氧树脂潜伏性固化剂[P].CN03115860,2004.
[31]郑国兵,郑亚萍,吴非.脲衍生物对环氧树脂/双氰胺体系促进作用的研究[J].中国塑料,2013,27(3):47-52.
[32]娄春华,马立群,王雅珍.双氰胺固化环氧树脂促进剂的研制[J].精细石油化工,2009,26(4):29-32.
[33]李彦玲,高堂铃,高洁,等.苯基缩水甘油醚改性2-甲基咪哩促进剂的研究[J].化学与黏合,2016,38(6):417-419.
[34]何尚锦,石可瑜,张珍坤,等.扩链脲改性环氧树脂E-51/双氰双胺(dicy)体系的固化行为[J].应用化学,2001,18(11):857-860.
[35]李瑞珍.新型咪唑类环氧固化促进剂[J].热固性树脂,1994,33(1):34-37.
[36]程秀莲,杨莹,刘运斌,等.酒石酸改性咪唑制备工艺及性能研究[J].粘接,2016,37(11):35-38.
[37]陈平.苄基二甲胺/双氰胺/环氧树脂体系固化物性能的研究[J].工程塑料应用,1992,10(1):11-14.
[38]高玉,余云照,赵彤.双氰胺与间苯二酚在环氧树脂固化中协同作用的研究[C].第十次全国环氧树脂应用技术学术交流会论文集,2003.
[39]唐卿珂,黄琴琴.溶剂对环氧树脂/双氰胺体系固化反应及覆铜板性能的影响[C].第九届全国印制电路学术年会论文集,2012.