用硫酸直接浸出—离子交换—铵盐沉淀法从石煤钒矿中提取五氧化二钒的试验研究
|
摘要
研究了从石煤钒矿中回收五氧化二钒。石煤钒矿破碎至90%以上通过0.15mm(100目)标准筛;在加热和有添加剂存在条件下,用硫酸直接浸出钒;浸出浆液调整酸度,固液分离;浸出液氧化除杂后用离子交换树脂吸附解吸钒;解吸液净化、沉淀偏钒酸铵,偏钒酸铵脱水、脱氨,获得五氧化二钒产品。结果表明:试验条件下,钒浸出率在76%以上,氧化除杂率为98.81%,离子交换回收率为98.23%,沉淀率为97.63%,脱水、脱氨回收率为99.05%,钒综合回收率为71.40%;所得五氧化二钒产品质量优于YB/T 5304-2006冶金98级标准。
Recovery of vanadium pentoxide from stone coal vanadium ore has been studied.Stone coal vanadium ore was crushed to 90% pass 100 mesh(0.15 mm) standard sieve,then vanadium was direct leached out using sulfuric acid under heating and additive.pH of the leaching slurry was first adjusted,then solid and liquid was separated.Vanadium in the liquid cleaned and oxidated was enriched by ion-exchange resin and precipitated using ammonium chloride to obtain ammonium metavanadate.By dehydration and deamination processes,the vanadium pentoxide product was obtained.The results showed that under test conditions,vanadium leaching rate was over 76%,vanadium recovery rate was 98.81% in cleaning and oxidation,98.23% in ion-exchange,97.63% in precipitation,and 99.05% in dehydration and deamination.Vanadium overall recovery was 71.40%.The vanadium pentoxide product quality was better than YB/T 5304—2006 metallurgy 98 standard.
Recovery of vanadium pentoxide from stone coal vanadium ore has been studied.Stone coal vanadium ore was crushed to 90% pass 100 mesh(0.15 mm) standard sieve,then vanadium was direct leached out using sulfuric acid under heating and additive.pH of the leaching slurry was first adjusted,then solid and liquid was separated.Vanadium in the liquid cleaned and oxidated was enriched by ion-exchange resin and precipitated using ammonium chloride to obtain ammonium metavanadate.By dehydration and deamination processes,the vanadium pentoxide product was obtained.The results showed that under test conditions,vanadium leaching rate was over 76%,vanadium recovery rate was 98.81% in cleaning and oxidation,98.23% in ion-exchange,97.63% in precipitation,and 99.05% in dehydration and deamination.Vanadium overall recovery was 71.40%.The vanadium pentoxide product quality was better than YB/T 5304—2006 metallurgy 98 standard.
引文
[1]蔡晋强,张顶列,巴陵,等.石煤提钒现状与市场浅析[J].稀有金属与硬质合金,1990(3):32-34.
[2]王永双,李国良.我国石煤提钒及综合利用综述[J].钒钛,1993(4):21-31.
[3]游先军,田宗平,李力,等.从湘西黑色页岩中提取钒的工艺研究[J].湿法冶金,2008,27(1):31-34.
[4]田宗平,魏祥晖,李力,等.从黑色岩系钒矿石中提取五氧化二钒的新工艺[J].湿法冶金,2011,30(1):37-40.
[5]邓克,游先军,田宗平.石煤旋窑焙烧工艺研究[J].湿法冶金,2009,28(2):84-87.
[6]田宗平,王永青,李力,等.石煤钒矿提取五氧化二钒工艺研究与工业实践[J].无机盐工业,2011,43(3):39-42.
[7]鲁兆伶,谷万成.从石煤中提取钒的焙烧试验研究[J].湿法冶金,2009,28(2):88-91.
[8]田宗平,游先军,刘志平,等.在浆法石煤提钒饱和树脂的洗脱除杂及精钒制备工艺研究[J].矿冶工程,2007,27(8):74-76.
[9]陈庆根.石煤钒矿提钒工艺技术的研究进展[J].矿产综合利用,2009(2):30-33.
[10]陈庆根.无盐焙烧酸法提取五氧化二钒的新工艺研究[J].矿产综合利用,2010(5):23-26.
[2]王永双,李国良.我国石煤提钒及综合利用综述[J].钒钛,1993(4):21-31.
[3]游先军,田宗平,李力,等.从湘西黑色页岩中提取钒的工艺研究[J].湿法冶金,2008,27(1):31-34.
[4]田宗平,魏祥晖,李力,等.从黑色岩系钒矿石中提取五氧化二钒的新工艺[J].湿法冶金,2011,30(1):37-40.
[5]邓克,游先军,田宗平.石煤旋窑焙烧工艺研究[J].湿法冶金,2009,28(2):84-87.
[6]田宗平,王永青,李力,等.石煤钒矿提取五氧化二钒工艺研究与工业实践[J].无机盐工业,2011,43(3):39-42.
[7]鲁兆伶,谷万成.从石煤中提取钒的焙烧试验研究[J].湿法冶金,2009,28(2):88-91.
[8]田宗平,游先军,刘志平,等.在浆法石煤提钒饱和树脂的洗脱除杂及精钒制备工艺研究[J].矿冶工程,2007,27(8):74-76.
[9]陈庆根.石煤钒矿提钒工艺技术的研究进展[J].矿产综合利用,2009(2):30-33.
[10]陈庆根.无盐焙烧酸法提取五氧化二钒的新工艺研究[J].矿产综合利用,2010(5):23-26.