Large areas of Latvia are contaminated with industrial waste: metallurgical slag, fly-ash, etching refuse, peat, and coal ash as well as glass waste which often contain dangerous substances. From the environmental point of view this waste should be neutralised. As this waste also contains valuable chemical compounds, it can be considered as a raw material for the generation of new materials. One method of utilisation is to produce recycled materials — street plates, decorative tiles, or floor tiles. Dense sintered glassceramics with a water uptake of 0.34–3.23 wt. % , a final density of 2.93–3.05 g/cm3, and a bending strength of 80–96 MPa have been created from industrial waste. The mast chemically durable glassceramics contained clay additions. Thus, the material containing only waste had a durability (mass loss) of 3.02 % in 0.1 N HCl, while the composition containing 30 % clay addition had a durability of 0.2 % in 0.1 N HCl.