• 责任者：Jiang Xiaoqian (School of Materials Science and Technology ; China University of Geosciences ; Beijing 100083 ; China) ; Li Jinhong
• 刊名：Acta Petrologica et Mineralogica
• 出版年：2009
• 卷期：28(6)
• 关键词：矿相学 ; ore microscopy
• 页码：p.675-679
• 图表：5 illus., 1 table, 9 refs.
• 分类号：0700
• issnNo：ISSN1000-6524
• isbnNo：CN11-1966/P

The aluminate cement clinker was successfully synthesized from starting materials of barium carbonate, alumina and calcium carbonate by designing mineral phase composition sintered at different temperatures. The formation mechanism of cement clinker was investigated by XRD and SEM. The results show that BaAl₂O₄ is mainly formed at relatively low temperatures, and then CaAl₂O₄ obviously increases with the increase of temperature in forming solid solution of BaAl₂O₄ and CaAl₂O₄.