Quantitative evaluation of the adhesion of bioactive glasses onto Ti6Al4V substrates
详细信息 查看全文
- 作者：A. Matinmanesh
- 关键词：Biomedical implants ; Bioactive glass coating ; Adhesion ; Fracture toughness ; Residual stresses
- 刊名：Materials & Design
- 出版年：2016
- 出版时间：5 May 2016
- 年：2016
- 卷：97
- 期：Complete
- 页码：213-221
- 全文大小：1005 K
文摘
- •
- <p id="p0005">A new method for applying a uniform thickness bioactive glass coating to a Ti6Al4V substrate was developed.p>
- •
- <p id="p0010">A novel methodology for quantifying the adhesive strength of enamelled bioactive glass coatings was presented.p>
- •
- <p id="p0015">Thinner glass coatings proved to have higher resistance against fracture than thicker ones.p>
- •
- <p id="p0020">Residual stresses in the glass/metal system were measured and it was found that they increase with the coating thickness.p>
- •
- <p id="p0025">It was found that as the coating thickness increased, the crack destabilized.p>