Microporous TiO2 was grown onto anatase TiO2 surface.
Adsorption of low concentration toluene was greatly enhanced.
Homojunction was formed at the interface of microporous TiO2 and anatase TiO2.
Separation of charge carriers were enhanced by growth of microporous TiO2.
Mineralization efficiency of toluene was significantly improved.