Graded cermets were prepared by introducing nitrogen at different sintering stages.
A high nitrogen activity could promote the dissolution of the rim phase.
The high nitrogen potential was favorable to the formation of WC and free carbon.
A harden surface layer formed in the graded cermets treated at cooling stage.
The surface hardness of cermets nitrided at cooling stage increased significantly.