TiO2/TiC0.7N0.3 coatings were prepared by ball milling followed by oxidation.
In situ co-doping of C and N with simultaneous TiO2 formation was observed.
Improved photocatalytic activity under UV/visible light was noticed.
Synergism in co-doping and heterojunction formation promoted carrier separation.