Microstructure and shear strength of brazed joints between Ti(C,N)-based cermet and steel with CuAgTi filler metal
详细信息 查看全文
- 作者：Yong Jing ; Qingqing Yang ; yqqah@sina.com" class="auth_mail" title="E-mail the corresponding author ; Weihao Xiong ; Bin Huang ; Baolong Li ; Man Zhang
- 关键词：Vacuum brazing ; Ti(C ; N)-based cermets ; CuAgTi filler metal ; Microstructure ; Shear strength
- 刊名：Journal of Alloys and Compounds
- 出版年：2016
- 出版时间：15 October 2016
- 年：2016
- 卷：682
- 期：Complete
- 页码：525-530
- 全文大小：2408 K
文摘
- •
Filler metal consisted of Cu- and Ag-based solid solution and Cu
Ti compounds.- •
The formation of Cu
NiTi solid solution was depended on brazing temperature.- •
Shear strength of joints reached 260 MPa after brazing at 910 °C for 30 min.
- •
Fracture surfaces were located within filler metal after brazing at 910 °C for 30 min.