Optimization, characterization and nanofiltration properties test of MWNTs/polyester thin film nanocomposite membrane

详细信息    查看全文

• 作者：Huiqing Wu ; Beibei Tang ; ^{bbtang@fudan.edu.cn} ; Peiyi Wu ; ^{peiyiwu@fudan.edu.cn}
• 关键词：Multi-walled carbon nanotubes ; Nanocomposite ; Nanofiltration ; Interfacial polymerization
• 刊名：Journal of Membrane Science
• 出版年：2013
• 出版时间：1 February, 2013
• 年：2013
• 卷：428
• 期：Complete
• 页码：425-433
• 全文大小：1396 K

文摘

MWNTs/polyester thin film nanocomposite (TFN) membranes were prepared through an improved process by interfacial polymerization of triethanolamine (TEOA) and trimesoyl chloride (TMC) on the polysulfone (PSf) supporting membrane in the presence of multi-walled carbon nanotubes (MWNTs). The effect of MWNTs concentration and surfactant species in the aqueous phase as well as the reaction time of interfacial polymerization on the membrane properties were investigated. The water permeability increased as the MWNTs concentration in aqueous phase increased up to 0.5 mg/mL, reaching a maximum which was nearly double that of the thin film membrane without MWNTs, while the membrane rejection kept increasing dramatically. Compared with cationic (CTAB) and non-ionic (Triton X-100) surfactants, anionic (SDS) surfactant was more suitable for the preparation of TFN membrane. The reaction time determined the extent of interfacial polymerization and the integrality of surface skin layer. Furthermore, the nanofiltration properties of the MWNTs/polyester TFN membrane were tested by examining the separation performance of different feed solutions, feed concentrations, feed pHs at 0.6 MPa operating pressure. Additionally, the MWNTs/polyester TFN membrane exhibited a good long-term stability.