Effect of Ageing at 700 ¡ãC on Microstructure and Mechanical Properties of S31042 Heat Resistant Steel

详细信息    查看全文

• 作者：Jing-zhong WANG ; Zheng-dong LIU ; Han-sheng BAO ; Shi-chang CHENG ; Bin WANG
• 关键词：ageing ; microstructure ; mechanical property ; precipitated phase
• 刊名：Journal of Iron and Steel Research, International
• 出版年：2013
• 出版时间：April, 2013
• 年：2013
• 卷：20
• 期：4
• 页码：54-58
• 全文大小：659 K

文摘

To investigate the effect of high temperature ageing on the microstructure and mechanical properties of S31042 steel, solid solution treatment at 700 ¡ãC was carried out for various time from 10 to 6000 h. Experimental results showed that the change of mechanical properties is closely related to the amount of precipitated phases. During ageing from 10 to 300 h, precipitation in the tested steel increases rapidly, and correspondingly, the high temperature yield strength and room temperature hardness of tested steel increase rapidly. Meanwhile, the thickness of the secondary phase on grain boundaries widens sharply and the room temperature Charpy impact absorb energy decreases. Ageing beyond 300 h, the precipitation in the steel increases gradually and the precipitates coarsen to a certain extent. The high temperature yield strength of the steel keeps stable, and the room temperature Charpy impact energy and hardness decrease slowly. Ageing beyond 3000 h, the mechanical properties of the steel tend to be stable. The main precipitates are M₂₃C₆, NbCrN and NbC in the tested steel.