Effect of microfibrillated cellulose addition on thermal properties of three grades of urea-formaldehyde resin

详细信息    查看全文

• 作者：Byung-Dae Park^a ; ^{byungdae@knu.ac.kr} ; Nadir Ayrilmis^b ; ^{nadiray@istanbul.edu.tr} ; Jin Heon Kwon^c ; ^{kwon@kangwon.ac.kr} ; Tae Hyung Han^c ; ^{thhan212@kangwon.ac.kr}
• 关键词：Microfibrillated cellulose ; Thermal stability ; Urea-formaldehyde ; Formaldehyde emission grade
• 刊名：International Journal of Adhesion and Adhesives
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：72
• 期：Complete
• 页码：75-79
• 全文大小：551 K
• 卷排序：72

文摘

Three grades of liquid urea-formaldehyde (UF) resin with different formaldehyde emission levels such as super E0 (SE0), E0 and E1 were modified by adding different amounts of microfibrillated cellulose (5 wt% MFC and 95 wt% water) that had been isolated by mechanical disintegration of pulp fibers. Thermal properties of these UF resins were investigated to understand thermal curing and degradation behaviors of the modified UF resins, using differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). The DSC thermograms showed an exothermic curing reaction, and the curing peak temperature of modified UF resins heavily depended on the emission resin grade with an increasing order from E1, E0 to SE0. The addition of MFC suspension into the UF resins gradually increased curing peak temperature suggesting a decrease in the resin reactivity. TGA results showed three main thermal degradation temperatures for the modified UF resins except the SE0 UF resin, which had four degradation temperatures.