文摘
Nanofibers of CeO2 and CuO/CeO2 composite were synthesized using electrospinning. Prepared nanofibers were characterized by SEM, XRD, EDX, XPS and FTIR. Green ceria has exhibit bigger diameter nanofiber in comparison with composite. The average diameter of CeO2 nanofibers was observed of 130 nm. The minimum average diameter of CuO/CeO2 nanofibers was 98 nm for 50 mol. % Cu.