Tribocorrosion behavior of the CrN coating in NaCl solution was investigated. The CrN coating showed excellent corrosion resistance and wear resistance. The CrN coating exhibited poor tribocorrosion performance in NaCl solution. Multi-scale Cl ion corrosion occurred simultaneously during the tribocorrosion. Force-corrosion synergy interaction induced the multi-degradation failure.